TECARIM 1500 yellow

PA 6 C modified

TECARIM 1500 is a PA6 block copolymer processed using the reaction injection molding process. Its elastomer component makes this a tough material capable of withstanding high levels of stress.


Chemical designation
PA 6 C (Cast polyamide 6)
1,11 g/cm3

Main Features

  • high toughness
  • resistant to many oils, greases and fuels
  • electrically insulating
  • good slide and wear properties
  • good wear properties
  • good impact strength

Target industries

Technical details

  • Mechanical properties
    Mechanical propertiesValueUnitParameterNorm
    Tensile strength at yield53MPa50mm/minDIN EN ISO 527-2
    Elongation at yield13%50mm/minDIN EN ISO 527-2
    Elongation at break58%50mm/minDIN EN ISO 527-2
    Flexural strength73MPa2mm/min, 10 NDIN EN ISO 178
    Modulus of elasticity
    (flexural test)
    2200MPa2mm/min, 10 NDIN EN ISO 178
    Compression strength14/26/53MPa1% / 2% / 5%EN ISO 604
    Compression modulus2100MPa5mm/min, 10 NEN ISO 604
    Impact strength (Charpy)n.b.kJ/m2max. 7,5JDIN EN ISO 179-1eU
    Notched impact strength (Charpy)16kJ/m2max. 7,5JDIN EN ISO 179-1eA
    Ball indentation hardness95MPaISO 2039-1
    Modulus of elasticity
    (tensile test)
    2200MPa1mm/minDIN EN ISO 527-2
    Tensile strength53MPa50mm/minDIN EN ISO 527-2
  • Thermal properties
    Thermal propertiesValueUnitParameterNorm
    Glass transition temperature53CDIN EN ISO 11357
    Melting temperature216CDIN EN ISO 11357
    Service temperature160Cshort termNN
    Thermal expansion (CLTE)1310-5*1/K23-60°C, long.DIN EN ISO 11359-1;2
    Thermal expansion (CLTE)1310-5*1/K23-100°C, long.DIN EN ISO 11359-1;2
    Service temperature95Clong termNN
    Specific heat1.7J/(g*K)ISO 22007-4:2008
    Thermal conductivity0.32W/(k*m)ISO 22007-4:2008
  • Electrical properties
    Electrical propertiesValueUnitParameterNorm
    surface resistivity1014ODIN IEC 60093
    volume resistivity1014O*cmDIN IEC 60093
  • Other properties
    Other propertiesValueUnitParameterNorm
    Resistance to hot water/ bases(+)--
    Resistance to weathering---
    Flammability (UL94)HB-corresponding toDIN IEC 60695-11-10;
    Water absorption1.2%24h / 96h (23°C)DIN EN ISO 62