TECAFORM AH black

POM-C black

add to list
product enquiry
request sample
Request machined part
Request customised profile
Request customised tube
In addition to TECAFORM AH natural (POM-C), which is white in colour, a black acetal version is also available; TECAFORM AH black. POM-C black is a porosity free copolymer acetal material manufactured by Ensinger under the tradename TECAFORM AH black in standard stock shapes for machining, and is extruded in sheet, rod and tube. This POM black material exhibits good chemical resistance, high strength, rigidity and hardness as well good sliding and wear properties. Additionally this black acetal can be suitable for direct contact with food and has improved UV protection for outdoor use. Ensinger manufactures black acetal (TECAFORM AH black) in various shapes such as delrin tube, delrin rod and delrin sheet.

Compliances

Facts

Chemical designation
POM-C (Polyacetal (Copolymer))
Colour
black
Alternative colours available
white blue
Density
1.41 g/cm3

Main Features

  • high toughness
  • high strength
  • high stiffness
  • good slide and wear properties
  • good chemical resistance
  • difficult to bond
  • good machinability

Target industries

mechanical engineering
oil and gas industry
automotive industry
food technology
aircraft and aerospace technology

Downloads

Datasheet (PDF)

Technical details

  • product-technical-detail-collapse-item-0-lvl-1
    Mechanical properties Value Unit Parameter Norm
    Modulus of elasticity
    (tensile test)    		 2800 MPa 1mm/min DIN EN ISO 527-2
    Tensile strength 67 MPa 50mm/min DIN EN ISO 527-2
    Tensile strength at yield 67 MPa 50mm/min DIN EN ISO 527-2
    Elongation at yield (tensile test) 9 % 50mm/min DIN EN ISO 527-2
    Elongation at break (tensile test) 32 % 50mm/min DIN EN ISO 527-2
    Flexural strength 91 MPa 2mm/min, 10 N DIN EN ISO 178
    Modulus of elasticity
    (flexural test)    		 2600 MPa 2mm/min, 10 N DIN EN ISO 178
    Compression modulus 2300 MPa 5mm/min, 10 N EN ISO 604
    Compression strength 20/35/68 MPa 1% / 2% / 5% EN ISO 604
    Impact strength (Charpy) 150 kJ/m2 max. 7,5J DIN EN ISO 179-1eU
    Notched impact strength (Charpy) 6 kJ/m2 max. 7,5J DIN EN ISO 179-1eA
    Shore hardness 82 D DIN EN ISO 868
  • product-technical-detail-collapse-item-1-lvl-1
    Thermal properties Value Unit Parameter Norm
    Glass transition temperature -60 C DIN EN ISO 11357
    Melting temperature 166 C DIN EN ISO 11357
    Thermal conductivity 0.39 W/(k*m) ISO 22007-4:2008
    Specific heat 1.4 J/(g*K) ISO 22007-4:2008
    Service temperature 140 C short term NN
    Service temperature 100 C long term NN
    Thermal expansion (CLTE) 13 10-5*1/K 23-60°C, long. DIN EN ISO 11359-1;2
    Thermal expansion (CLTE) 14 10-5*1/K 23-100°C, long. DIN EN ISO 11359-1;2
  • product-technical-detail-collapse-item-2-lvl-1
    Electrical properties Value Unit Parameter Norm
    surface resistivity 1014 Ω Silver electrode, 23°C, 12% r.h. -
    volume resistivity 1014 Ω*cm Silver electrode, 23°C, 12% r.h. -
    Dielectric strength 38 kV/mm 23°C, 50% r.h. ISO 60243-1
    Resistance to tracking (CTI) 600 V Platin electrode, 23°C, 50% r.h., solvent A DIN EN 60112
  • product-technical-detail-collapse-item-3-lvl-1
    Other properties Value Unit Parameter Norm
    Resistance to hot water/ bases (+) -
    Flammability (UL94) HB corresponding to DIN IEC 60695-11-10;
    Resistance to weathering (+) -
    Water absorption 0.05 / 0.1 % 24h / 96h (23°C) DIN EN ISO 62
  • product-technical-detail-collapse-item-4-lvl-1
    Relative costs Value Unit Parameter Norm
    Relative costs EU from € to €€€€€€ €