TECAFIL PC FRT GF10 black - 1.75 mm - 2000 g

Flame-retardant PC filament on 2000 g spool

add to list
product inquiry
request sample

TECAFIL PC FRT GF10 - 1.75 - 2000g is a flame-retardant PC filament designed for the rail industry and has the same material properties as TECAFIL PC FRT GF10 - 1.75. With 2000 g instead of 750 g, this filament is ideal for larger applications and reduces the frequency of spool changes. Full technical details can be found on the product page for TECAFIL PC FRT GF10 - 1.75.

Compliances

Facts

Chemical designation
PC (Polycarbonate)
Colour
black
Density
1.37 g/cm3

Main Features

  • electrically insulating
  • tested according to EN 45545
  • flame retardant as per FAR 25.853
  • flame retardant according to UL94 V-0

Target industries

electronics
Railway Interiors
automotive industry
aircraft and aerospace interiors

Downloads

Datasheet (PDF)

Technical details

  • product-technical-detail-collapse-item-0-lvl-1
    General material information Value Unit Parameter Norm
    Diameter 1,75 +/- 0,05 mm -
    Spool measurements Ø 300 mm outer diameter -
    Spool measurements 100 mm width -
    Spool measurements Ø 52 mm holder -
    Spool Material Polycarbonate - -
    Filament Load per Spool 2000 g -
  • product-technical-detail-collapse-item-1-lvl-1
    Mechanical properties Value Unit Parameter Norm
    Tensile strength 68,9 MPa 5mm/min, Orientation XY DIN EN ISO 527-2
    Tensile strength 77,4 MPa 5mm/min, Orientation XZ DIN EN ISO 527-2
    Tensile strength 26,0 MPa 5mm/min, Orientation ZX DIN EN ISO 527-2
    Modulus of elasticity
    (tensile test)    		 4402 MPa 5mm/min, Orientation XZ DIN EN ISO 527-2
    Modulus of elasticity
    (tensile test)    		 3792 MPa 5mm/min, Orientation XY DIN EN ISO 527-2
    Modulus of elasticity
    (tensile test)    		 1894 MPa 5mm/min, Orientation ZX DIN EN ISO 527-2
    Elongation at break (tensile test) 4,2 % 5mm/min, Orientation XY DIN EN ISO 527-2
    Elongation at break (tensile test) 3,7 % 5mm/min, Orientation XZ DIN EN ISO 527-2
    Elongation at break (tensile test) 1,9 % 5mm/min, Orientation ZX DIN EN ISO 527-2
    Flexural strength 100,7 MPa 2mm/min, Orientation XY DIN EN ISO 178
    Flexural strength 113,5 MPa 2mm/min, Orientation XZ DIN EN ISO 178
    Flexural strength 69,0 MPa 2mm/min, Orientation ZX DIN EN ISO 178
    Modulus of elasticity
    (flexural test)    		 2960 MPa 2mm/min, Orientation XY DIN EN ISO 178
    Modulus of elasticity
    (flexural test)    		 3610 MPa 2mm/min, Orientation XZ DIN EN ISO 178
    Modulus of elasticity
    (flexural test)    		 2240 MPa 2mm/min, Orientation ZX DIN EN ISO 178
  • product-technical-detail-collapse-item-2-lvl-1
    Thermal properties Value Unit Parameter Norm
    Glass transition temperature 115 C ASTM D 3418
    Melting temperature - - DIN EN ISO 11357
    Deflection temperature 94 C HDT-A ISO-R 75 Method A
    Service temperature 100 C short term -
    Service temperature 80 C long term -
    Thermal expansion (CLTE) - 10-5*1/K DIN EN ISO 11359-1;2
  • product-technical-detail-collapse-item-3-lvl-1
    Other properties Value Unit Parameter Norm
    Moisture absorption 0,05 % DIN EN ISO 62
    Melt flow index (MFI) 7,4 g/10 min 300°C / 1,2kg DIN EN ISO 1133
    Flammability (UL94) 1,5 & 5,0 mm UL94 - V0 // 125x13mm DIN IEC 60695-11-10;
    Flammability (UL94) V0 DIN IEC 60695-11-10;
    Flammability 1,5 & 5,0 mm DIN EN 45545-2:2023: R1 - HL1, HL2, HL3 EN 45545-2:2016
    Flammability 1,5 & 5,0 mm Smoke Density, FAR/CS 25.853 (d) App. F Part V FAR 25.853
    Flammability 1,5 & 5,0 mm Heat release (OSU), FAR/CS 25.853 (d) App. F Part IV FAR 25.853
    Flammability 1,5 & 5,0 mm Gas Toxicity, AITM 3-0005 (issue 2) // Boeing BSS 7239 FAR 25.853
    Flammability 1,5 & 5,0 mm 15 sec. Horizontal Bunsen Burner test, FAR/CS 25.853 (a) App. F Part I (a)(1)(v) FAR 25.853
    Flammability 1,5 & 5,0 mm 12 sec. Vertical Bunsen Burner test, FAR/CS 25.853 (a) App. F Part I (a)(1)(ii) FAR 25.853
    Flammability 1,5 & 5,0 mm 15 sec. Horizontal Bunsen Burner test, FAR/CS 25.853 (a) App. F Part I (a)(1)(iv) FAR 25.853
    Flammability 1,5 & 5,0 mm 60 sec. Vertical Bunsen Burner test, FAR/CS 25.853 (a) App. F Part I (a)(1)(i) FAR 25.853
  • product-technical-detail-collapse-item-4-lvl-1
    Processing parameter Value Unit Parameter Norm
    Nozzle temperature 300 - 330 C -
    Max. melt temperature 350 C -
    Print bed temperature 100 - 130 C -
    Build chamber temperature 80 - 110 C -
    Nozzle diameter 0,4 - 0,6 mm -
    Print speed 25 - 40 mm/s -
    Fan speed 0 % -
  • product-technical-detail-collapse-item-5-lvl-1
    Predrying Value Unit Parameter Norm
    Drying temperature 100 C -
    Drying time 8 h -