TECATRON PVX black

PPS modified by carbon fibres, PTFE and graphite

add to list
product enquiry
request sample
Through TECATRON PVX black, Ensinger offers a filled PPS (PPS CS CF TF), which is a specially modified for use in sliding applications. The material contains 10% each of PTFE, graphite and carbon fibres which are added to the PPS to facilitate bearing and wear applications. The additives of the PPS compound result in an optimum coefficient of friction value, that makes the material ideally suited to dry running conditions. So TECATRON PVX is a bearing grade PPS that is suitable for high load applications, under high temperatures, and the effects of chemicals and steam. The PPS compound perfectly combines good mechanical properties with excellent thermal and chemical resistance properties.

Compliances

Facts

Chemical designation
PPS (Polyphenylensulfide)
Colour
black
Density
1.5 g/cm3

Main Features

  • good heat deflection temperature
  • very good slide and wear properties
  • very good chemical resistance
  • inherent flame retardant
  • high stiffness
  • high dimensional stability
  • high creep resistance

Target industries

mechanical engineering
vacuum technology
oil and gas industry
aircraft and aerospace technology
automotive industry

Downloads

Datasheet (PDF)
Product handling (PDF)

Technical details

  • product-technical-detail-collapse-item-0-lvl-1
    Mechanical properties Value Unit Parameter Norm
    Modulus of elasticity
    (tensile test)    		 4600 MPa 1mm/min DIN EN ISO 527-2
    Tensile strength 53 MPa 50mm/min DIN EN ISO 527-2
    Tensile strength at yield 53 MPa 50mm/min DIN EN ISO 527-2
    Elongation at yield (tensile test) 2 % 50mm/min DIN EN ISO 527-2
    Elongation at break (tensile test) 2 % 50mm/min DIN EN ISO 527-2
    Flexural strength 91 MPa 2mm/min, 10 N DIN EN ISO 178
    Modulus of elasticity
    (flexural test)    		 4800 MPa 2mm/min, 10 N DIN EN ISO 178
    Compression modulus 3300 MPa 5mm/min, 10 N EN ISO 604
    Compression strength 19/36/89 MPa 1% / 2% / 5% EN ISO 604
    Impact strength (Charpy) 14 kJ/m2 max. 7,5J DIN EN ISO 179-1eU
    Shore hardness 85 D DIN EN ISO 868
  • product-technical-detail-collapse-item-1-lvl-1
    Thermal properties Value Unit Parameter Norm
    Glass transition temperature 94 C DIN EN ISO 11357
    Melting temperature 281 C DIN EN ISO 11357
    Thermal conductivity 0.58 W/(k*m) ISO 22007-4:2008
    Specific heat 0.9 J/(g*K) ISO 22007-4:2008
    Service temperature 260 C short term NN
    Service temperature 230 C long term NN
    Thermal expansion (CLTE) 5 10-5*1/K 23-60°C, long. DIN EN ISO 11359-1;2
    Thermal expansion (CLTE) 6 10-5*1/K 23-100°C, long. DIN EN ISO 11359-1;2
    Thermal expansion (CLTE) 13 10-5*1/K 100-150°C, long. DIN EN ISO 11359-1;2
  • product-technical-detail-collapse-item-2-lvl-1
    Electrical properties Value Unit Parameter Norm
    surface resistivity 104 -1010 Ω DIN EN 61340-2-3
    volume resistivity 107-1012 Ω*cm DIN EN 61340-2-3
  • product-technical-detail-collapse-item-3-lvl-1
    Other properties Value Unit Parameter Norm
    Resistance to hot water/ bases + - -
    Flammability (UL94) V0 - corresponding to DIN IEC 60695-11-10;
    Resistance to weathering (+) - -
    Water absorption <0.01 % 24h / 96h (23°C) DIN EN ISO 62
  • product-technical-detail-collapse-item-4-lvl-1
    Relative costs Value Unit Parameter Norm
    Relative costs EU from € to €€€€€€ €€€

Stock program