TECASINT 2021 black

Polyimide with 15% graphite

TECASINT 2021 is a plastic reinforced with 15% graphite and based on the base polymer TECASINT 2011. It is particularly suitable for tribological applications owing to its improved friction and wear behavior. Thanks to its self lubricating property, TECASINT 2021 is well suited to lubricated and dry applications.

Facts

Chemical designation
PI (Polyimide)
Color
black
Density
1.45 g/cm3

Main Features

  • very good slide and wear properties
  • very good thermal stability
  • high thermal and mechanical capacity
  • good wear resistance
  • resistance against high energy radiation
  • high creep resistance
  • good chemical resistance
  • sensitive to hydrolysis in higher thermal range

Target industries

Downloads

Technical details


  • product-technical-detail-collapse-item-0-lvl-1
    Mechanical properties Value Unit Condition Test Method
    Notched impact strength (Charpy) 2.9 kJ/m2 max 7.5 J DIN EN ISO 179-1
    Impact strength (Charpy) 36.7 kJ/m2 max 7.5 J DIN EN ISO 179-1
    Shore hardness 87 Shore D DIN EN ISO 868
    Tensile strength 101 MPa 50 mm/min DIN EN ISO 527-1
    Modulus of elasticity
    (tensile test)
    4400 MPa 1 mm/min DIN EN ISO 527-1
    Flexural strength 145 MPa 10 mm/min DIN EN ISO 178
    Modulus of elasticity
    (flexural test)
    4000 MPa 2 mm/min DIN EN ISO 178
    Compression modulus 1900 MPa 1 mm/min EN ISO 604
    Compressive strain at break 43 % 10 mm/min EN ISO 604
    Elongation at break (tensile test) 4.5 % 50 mm/min DIN EN ISO 527-1
    Compression strength 280 MPa 10 mm/min EN ISO 604
    Elongation at break (flexural test) 4.6 % 10 mm/min DIN EN ISO 178
    Compression strength 160 MPa 10mm/min, 10% strain EN ISO 604
  • product-technical-detail-collapse-item-1-lvl-1
    Thermal properties Value Unit Condition Test Method
    Glass transition temperature 357 C -
    Heat distortion temperature 335 C 1.8 MPa DIN 53 461
    Thermal expansion (CLTE) 4.5 10-5*1/K 50-200°C DIN 53 752
    Service temperature 260 C long-term -
    Thermal expansion (CLTE) 5.4 10-5*1/K 200-300°C DIN 53 752
  • product-technical-detail-collapse-item-2-lvl-1
    Other properties Value Unit Condition Test Method
    Flammability (UL94) V0 - corresponding to DIN IEC 60695-11-10;
    HZ-Catalogue yes - -
    HZ Technical guidelines yes lbs/in^2 -
    HZ Aerospace Brochure no - -
    Water absorption 0.61 % 24 h in water, 23°C DIN EN ISO 62
    Water absorption 1.69 % 24 h in water, 80°C DIN EN ISO 62