TECATEC PEI GW50 PL V01 natural

Glass fibre filled PPS composite plate

This polyphenylenesulfide (PPS) based material has been reinforced with 50 vol% glass fibre. PPS is a semi-crystalline, highly temperature resistant thermoplastic, which is known for its excellent chemical resistance. Good creep resistance and low water absorption are additional features of the PPS sheet. Thanks to the glass fibre fabric reinforcement, TECATEC PPS GW50 PL V01 natural offers high stiffness and strength at a competitive price. The mechanical properties of the glass filled plastic are retained even at high temperatures, since PPS has a continuous service temperature of over 200 °C.

This reinforced thermoplastic material also offers excellent electrical insulation and high resistance to leakage current and is therefore suitable for electrical applications.
Due to the inherent flame retardancy, the excellent chemical resistance and the high temperature resistance, PPS composite is ideally suited for demanding applications in transportation, safety engineering, oil and gas and general mechanical engineering. 

Just like the carbon fibre-reinforced material TECATEC PPS CW50 PL V01 natural, the glass filled thermoplastic TECATEC PPS GW50 PL V01 natural is manufactured in sheets with a thickness from 1 mm up to 95 mm, without any minimum order quantity.

Facts

Chemical designation
PEI (Polyetherimide)
Colour
natural
Density
1.9 g/cm3

Main Features

  • electrically insulating
  • inherent flame resistance
  • very good mechanical strength

Target industries

Downloads

Technical details


  • product-technical-detail-collapse-item-0-lvl-1
    General material information Value Unit Parameter Norm
    Fibre type E glass - -
    Fibre architecture US 7781 - -
    Fibre areal weight 296 g/m2 -
    Fibre volume content 50 % -
    Resin weight content 33.7 % -
    Areal weight finished product 446 g/m2 -
    Material widths 625x525 mm others on request
  • product-technical-detail-collapse-item-1-lvl-1
    Mechanical properties Value Unit Parameter Norm
    Tensile strength 450 MPa ISO 527-4
    Modulus of elasticity
    (tensile test)
    24000 MPa ISO 527-4
    Flexural strength 570 MPa ISO 14125
    Modulus of elasticity
    (flexural test)
    26000 MPa ISO 14125
    Compression strength 670 MPa ISO 14126
  • product-technical-detail-collapse-item-2-lvl-1
    Thermal properties Value Unit Parameter Norm
    Glass transition temperature 217 C -
    Service temperature 200 C short term -
    Service temperature 180 C long term -
    Thermal expansion (CLTE) 10 106*K-1 in 0° and 90° direction -
  • product-technical-detail-collapse-item-3-lvl-1
    Predrying Value Unit Parameter Norm
    Drying temperature 150 C -
    Drying time 4-6 h -

Stock program