TECAGLIDE black

Cast nylon with extremely good sliding and wear properties

TECAGLIDE black is a PA plastic which is manufactured in a casting process. This cast nylon is characterised by extremely good sliding and wear properties due to the addition of proprietary solid lubricants. Because of the combination of lubricity and high mechanical load properties, TECAGLIDE is considered one of the optimal solutions in our portfolio for sliding applications at high speeds, especially when it comes to the desire to manage friction while enhancing wear properties. As an example, this PA6 plastic can be used in mechanical engineering as plain bearings, guide rails or gear wheels just to name a few.
PA plastic TECAGLIDE is electrically insulating, extremely resistant to most oils and has a high degree of ductility and toughness. In addition, no external lubrication is required for most applications due to the material's unique property and performance profile. TECAGLIDE black is available from stock in all dimensions as plates and rods.

Facts

Chemical designation
PA 6 C (Cast polyamide 6)
Colour
black
Density
1.13 g/cm3

Main Features

  • electrically insulating
  • resistant to many oils, greases and fuels
  • good slide and wear properties
  • high toughness
  • good wear properties
  • high mechanical load capacity

Target industries

Technical details


  • product-technical-detail-collapse-item-0-lvl-1
    Mechanical properties Value Unit Parameter Norm
    Modulus of elasticity
    (tensile test)
    3200 MPa 1mm/min DIN EN ISO 527-2
    Tensile strength 76 MPa 50mm/min DIN EN ISO 527-2
    Tensile strength at yield 76 MPa 50mm/min DIN EN ISO 527-2
    Elongation at yield (tensile test) 14 % 50mm/min DIN EN ISO 527-2
    Elongation at break (tensile test) 18 % 50mm/min DIN EN ISO 527-2
    Flexural strength 103 MPa 2mm/min, 10 N DIN EN ISO 178
    Modulus of elasticity
    (flexural test)
    3100 MPa 2mm/min, 10 N DIN EN ISO 178
    Compression modulus 2500 MPa 5mm/min, 10 N EN ISO 604
    Compression strength 18/34/75 MPa 1% / 2% / 5% EN ISO 604
    Impact strength (Charpy) n.b. kJ/m2 max. 7,5J DIN EN ISO 179-1eU
    Notched impact strength (Charpy) 4 kJ/m2 max. 7,5J DIN EN ISO 179-1eA
    Shore hardness 79 D DIN EN ISO 868
  • product-technical-detail-collapse-item-1-lvl-1
    Thermal properties Value Unit Parameter Norm
    Glass transition temperature 45 C DIN EN ISO 11357
    Melting temperature 218 C DIN EN ISO 11357
    Heat distortion temperature C HDT, Method A ISO-R 75 Method A
    Thermal conductivity 0.38 W/(k*m) ISO 22007-4:2008
    Specific heat 1.7 J/(g*K) ISO 22007-4:2008
    Service temperature 130 C short term NN
    Service temperature 100 C long term NN
    Thermal expansion (CLTE) 11 10-5*1/K 23-60°C, long. DIN EN ISO 11359-1;2
    Thermal expansion (CLTE) 12 10-5*1/K 23-100°C, long. DIN EN ISO 11359-1;2
  • product-technical-detail-collapse-item-2-lvl-1
    Electrical properties Value Unit Parameter Norm
    surface resistivity 1014 DIN IEC 60093
    volume resistivity 1014 Ω*cm DIN IEC 60093
  • product-technical-detail-collapse-item-3-lvl-1
    Other properties Value Unit Parameter Norm
    Resistance to hot water/ bases (+) - -
    Flammability (UL94) HB - corresponding to DIN IEC 60695-11-10;
    Resistance to weathering - - -
    Water absorption 0.2 - 0.3 % 24h / 96h (23°C) DIN EN ISO 62
  • product-technical-detail-collapse-item-4-lvl-1
    Relative costs Value Unit Parameter Norm
    Relative costs EU from € to €€€€€€

Stock program