TECASINT 1061 black

Polyimide with 15 % graphite and 10 % PTFE

Starting with the base polymer TECASINT 1011, TECASINT 1061 with 15% graphite and 10% PTFE has been developed. Its properties include very low static friction and a low coefficient of friction. The material is self lubricating, which means it also has good properties in dry running conditions. TECASINT 1061 is suitable for low friction and low wear applications at medium temperatures (<200°C) and loads.

Facts

Chemical designation
PI (Polyimide)
Colour
black
Density
1,48 g/cm3

Main Features

  • very good slide and wear properties
  • high thermal and mechanical capacity
  • good wear resistance
  • resistance against high energy radiation
  • good chemical resistance
  • sensitive to hydrolysis in higher thermal range

Target industries

Technical details


  • Mechanical properties
    Mechanical propertiesValueUnitParameterNorm
    Notched impact strength (Charpy)3.9kJ/m2max 7.5 J, 23°CDIN EN ISO 179-1
    Impact strength (Charpy)25.8kJ/m2max 7.5 J, 23°CDIN EN ISO 179-1
    Shore hardness85-Shore D, 23°C-
    Tensile strength77MPa50 mm/min, 23°CDIN EN ISO 527-1
    Elongation at break2.9%50 mm/min, 23°CDIN EN ISO 527-1
    Modulus of elasticity
    (tensile test)
    4400MPa50 mm/min, 23°CDIN EN ISO 527-1
    Flexural strength120MPa10 mm/min, 23°CDIN EN ISO 178
    Modulus of elasticity
    (flexural test)
    4000MPa10 mm/min, 23°CDIN EN ISO 178
    Compression strength170MPa10 mm/min, 23°CEN ISO 604
    Elongation at break3.6%10 mm/min, 23°CDIN EN ISO 178
  • Thermal properties
    Thermal propertiesValueUnitParameterNorm
    Glass transition temperature353C-
    Service temperature-Clong-term-
  • Other properties
    Other propertiesValueUnitParameterNorm
    Water absorption0.64%24 h in water, 23°CDIN EN ISO 62
    Water absorption1.82%24 h in water, 80°CDIN EN ISO 62
    Flammability (UL94)V0-corresponding toDIN IEC 60695-11-10;