TECASINT 1031 black

polyimide with 40 % graphite

Starting with the base polymer TECASINT 1011, TECASINT 1031 has been developed. This material contains 40% graphite, unlike the starting material. TECASINT 1031 has a very high resistance to thermal ageing and improved self lubrication. Its other properties include minimised thermal elongation for dimensionally stable components and increased creep strength.

Facts

Chemical designation
PI (Polyimide)
Colour
black
Density
1,57 g/cm3

Main Features

  • very good thermal stability
  • very good slide and wear properties
  • good wear resistance
  • very high creep resistant
  • high thermal and mechanical capacity
  • resistance against high energy radiation
  • low thermal expansion
  • sensitive to hydrolysis in higher thermal range

Target industries

Technical details


  • Mechanical properties
    Mechanical propertiesValueUnitParameterNorm
    Notched impact strength (Charpy)3.6kJ/m2max 7.5 J, 23°CDIN EN ISO 179-1
    Impact strength (Charpy)16.5kJ/m2max 7.5 J, 23°CDIN EN ISO 179-1
    Shore hardness84-Shore D, 23°C-
    Tensile strength58MPa50 mm/min, 23°CDIN EN ISO 527-1
    Elongation at break1.6%50 mm/min, 23°CDIN EN ISO 527-1
    Modulus of elasticity
    (tensile test)
    6200MPa50 mm/min, 23°CDIN EN ISO 527-1
    Flexural strength83MPa10 mm/min, 23°CDIN EN ISO 178
    Modulus of elasticity
    (flexural test)
    5900MPa10 mm/min, 23°CDIN EN ISO 178
    Compression strength126MPa10 mm/min, 23°CEN ISO 604
    Compression modulus2700MPa10 mm/min, 23°CEN ISO 604
    Elongation at break1.4%10 mm/min, 23°CDIN EN ISO 178
  • Thermal properties
    Thermal propertiesValueUnitParameterNorm
    Glass transition temperature353C-
    Service temperature-Clong-term-
    Thermal expansion (CLTE)10-5*1/K200-300°CDIN 53 752
    Thermal expansion (CLTE)10-5*1/K50-200°CDIN 53 752
  • Other properties
    Other propertiesValueUnitParameterNorm
    Water absorption0.6%24 h in water, 23°CDIN EN ISO 62
    Flammability (UL94)V0-corresponding toDIN IEC 60695-11-10;